Structure and adhesion of nickel-phosphorus coatings plated on the nitrided 1.2343 (WCL) steel

Struktura i przyczepność powłok niklowych do stali 1.2343 (WCL) po procesie azotowania jarzeniowego

10.15199/28.2017.6.1

nr katalogowy: 111383
10.15199/28.2017.6.1

Streszczenie

Modern industry expects comprehensive solutions in terms of ensuring adequate exploitation properties of materials, such as high hardness, wear resistance, fatigue strength and corrosion resistance in aggressive environments. These requirements can be met via surface treatments, especially vigorously developed in recent years hybrid technologies, which merge various methods in the aspect of composite layers production. Those layers are characterized by complementing or entirely new properties in comparison to layers or coatings manufactured in separate processes. In this study the plasma nitriding process and electroless nickel plating are combined. In the production of composite layers consisting of surface layer and coating, in this particular case it is essential to ensure good adhesion of the Ni(P) coating to nitrided substrate. This paper presents microstructure (light microscopy), microhardness (crosssection and surface), surface roughness and scratch test results after different variants and steps of treatment of heat treated 1.2343 (WCL) steel. The study was conducted on the nitrided layers varying in structure and surface topography due to grinding prior to electroless nickel plating. The results show that heat treatment subsequent to electroless nickel plating leads to increase in composite layers’ hardness and adhesion of Ni(P) coating to nitrided layer. Moreover, Ni(P) coating might act as a solid lubricant in some cases.

Abstract

Celem badań było określenie wpływu struktury, twardości oraz rozwinięcia powierzchni warstwy azotowanej na stali 1.2343, a także procesu obróbki cieplnej powłoki Ni(P) na przyczepność powłoki niklowo-fosforowej do azotowanego podłoża. W pracy zawarto wyniki badań chropowatości powierzchni, mikrostruktury warstw kompozytowych, ich twardości oraz przyczepności

Słowa kluczowe

Keywords

Bibliografia

[1] Wierzchoń T.: Structure and properties of multicomponent and composite layers produced by combined surface engineering methods. Surface & Coatings Technology 180-181 (2004) 458÷464.
[2] Kula P.: Inżynieria warstwy wierzchniej. Wydawnictwo Politechniki Łódzkiej, Łódź (2000).
[3] Burakowski T., Wierzchoń T.: Surface engineering of metals, principles, equipments, technologies. CRC press Boca Raton, London (1999).
[4] Morita T., Inoue K., Ding X., Usui Y., Ikenaga M.: Effect of hybrid surface treatment composed of nitriding and DLC coating on friction-wear properties and fatigue strength of alloy steel. Materials Science & Engineering A 661 (2016) 105÷114.
[5] Winck L., Ferreira J., Araujo J., Manfrinato M., da Silva C.: Surface nitriding influence on the fatigue life behavior of ASTM A743 steel type CA6NM. Surface & Coatings Technology 232 (2013) 844÷850.
[6] Parkinson R.: Properties and applications of electroless nickel. Nickel Developement Institute, NiDI Technical Series No. 10 081 (1997).
[7] Funatani K., Kurosawa K.: Composite coatings improve engines. Advanced Materials & Processes 12 (1994) 27÷29.
[8] Wierzchoń T., Rudnicki R., Bogdański A., Fleszar A., Maranda-Niedbała A., Hering M., Niedbała R.: Opracowanie podstaw technologii wytwarzania warstw wieloskładnikowych antykorozyjnych i antyściernych na bazie kobaltu, niklu i chromu. Prace Naukowe Politechniki Warszawskiej z. 8 (1998) 23÷33.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 111383 "Structure and adhesion of..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2017-6 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2017-6

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma