Czasopismo | OCHRONA PRZED KOROZJĄ | Rocznik 2017 - zeszyt 11

The effect of bio-tolerated binder content on the corrosive behavior of RE-M-B in magnetic composites in sulphite solutions

Wpływ zawarości biotolerowalnego spoiwa na zachowanie korozyjne kompozytów magnetycznych RE-M-B w roztworach siarczanowych

10.15199/40.2017.11.4

nr katalogowy: 110440
10.15199/40.2017.11.4

Streszczenie

The purpose of this work was to analyze the effect of the new binder (extender) on the behavior of the magnetic composite in acidified sulphate environment. In the studies the magnetic powder with chemical formula Nd12Fe77Co5B6 (lower indices denotes atomic %) and biopolymer of which polymerization processes is carried out in low temperatures have been used. On the basis of the presented potentiokinetic polarization curves and changes in polarization resistance, the most favorable, in terms of corrosion resistance, composition of the Nd-Fe-B/biopolymer magnetic composite has been selected.

Abstract

Celem niniejszej pracy była analiza wpływu nowego spoiwa (wypełniacza) na zachowanie kompozytu magnetycznego Nd-Fe-B/biopolimer w zakwaszonym środowisku siarczanowym. W badaniach wykorzystano proszek magnetyczny o formule chemicznej Nd12Fe77Co5B6 (indeksy dolne oznaczają % atomowe). Jako spoiwa do konsolidacji proszku użyto biopolimeru, którego proces polimeryzacji przebiega w niskich temperaturach. Na podstawie zaprezentowanych krzywych potencjo kinetycznych oraz zmiany oporu polaryzacji wytypowano najkorzystniejszy pod względem odporności korozyjnej skład kompozytu.

Słowa kluczowe

Keywords

Bibliografia

[1] Klimecka-Tatar D. 2009. Modyfikowanie właściwości fizykochemicznych magnesów poprzez chemiczną obróbkę nanokrystalicznego proszku na bazie Nd-Fe-B. Częstochowa: Rozprawa doktorska. Politechnika Częstochowska.
[2] Klimecka-Tatar D., G. Pawłowska. S. Szymura. 2009. “Rola wstępnego trawienia powierzchni cząstek proszku MQP-B w kształtowaniu odporności korozyjnej magnesów wiązanych". Ochrona przed Korozją 52 (11) : 514-519.
[3] Langot C., M.I. Pers. M. Janicki. 2004. “Wykorzystanie systemu retencji magnetycznej Dyna w protetycznej rehabilitacji pacjenta". Prot Stomat. 54 : 100.
[4] Leonowicz M. 1996. Nowoczesne materiały magnetycznie twarde. Warszawa: Oficyna wydawnicza Politechniki Warszawskiej.
[5] Leonowicz M., J. J. Wysłocki. 2005. Współczesne magnesy. Warszawa: Wyd. Naukowo- Techniczne.
[6] Machnikowski I., J. Gładkowski M., Siedlecki T. Feder. 2002. “Zastosowanie precyzyjnych elementów retencyjnych u pacjentów z rozległymi brakami zębowymi". Prot. Stomat. 52 : 344-348.
[7] Meada Y., K. Nakao, K. Yagi, S. Matsuda. 2006. “Composite resin root coping with a keeper for magnetic attachment for replacing the missing coronal portion of a removable partial denture abutment". J. Prosthet. Dent. (96) : 139-142.
[8] Najgebauer M., J. Szczygłowski. 2011. "Kompozyty magnetyczne w maszynach elektrycznych". Elektryka zeszyt 4 (220) : 29-40.
[9] Pawłowska G., K. Radomska, D. Klimecka-Tatar. 2016. "Wpływ konsolidacji biopolimerem na charakterystyki korozyjne wiązanych magnesów Nd-(Fe.Co)-B". Ochrona przed Korozją 59 (7) : 256-259.
[10] Polski opis patenowy nr 195336.
[11] Radomska K., D. Klimecka-Tatar, G. Pawłowska. 2016. “Effect of the powder consolidation with biopolymer on the corrosion characteristics of bonded magnets based on Nd-(Fe,Co)-B". Ochrona przed Korozją 59 (4) : 128-131.
[12] Radomska K., G. Pawłowska, D. Klimecka-Tatar. 2016. “The effect of the corrosion process on the surface topography of bonded with biopolimer magnets Nd-Fe-B type". Czasopismo Techniczne. Y113 : 119-124.
[13] Skulj I., A. P. Douvalis, I. R. Harris. 2006. “Characterisation of oxidation products of modified Nd-Fe-B type magnets". Journal of Alloys and Compounds 407 : 304-313.
[14] Stabik J., A. Dybowska, A. Chrobak, G. Haneczok. 2011. “Właściwości magnetyczne kompozytów epoksydowych napełnionych proszkiem ferrytu strontu". LogosPress. : 465-470.
[15] Ślusarek B., D. Klimecka-Tatar, H. Bala, K. Gąsiarz. 2005. “Wpływ technologii konsolidacji proszków na własności magnetyczne. mechaniczne i korozyjne nanokrystalicznego materiału typu Nd-Fe-B". Ochrona przed Korozją 48 (11s/A) : 93.
[16] Ślusarek B., L. Długiewicz. 2006. “Obszar zastosowań proszkowych materiałów magnetycznych". Elektronika. konstrukcje. technologie. zastosowania 47 (8) : 45-49.
[17] Turek K., P. Liszowski, H. Figiel. 1993. “The kinetics of oxidation of Nd-Fe-B powders". IEEE 29 (6) : 2782-2784.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 110440 "The effect of bio-tolerat..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2017-11 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2017-11

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma