Corrosion properties of Ni-B/Al2O3 composites layers produced by electroless method

Właściwości korozyjne warstw kompozytowych Ni-B/Al2O3 wytwarzanych metodą bezprądową

10.15199/40.2017.7.1

nr katalogowy: 107488
10.15199/40.2017.7.1

Streszczenie

The paper presents results of studies of alloy composite layers of Ni-B/ Al2O3 produced by electroless method on steel substrate. As the dispersion phase is the powder of aluminum oxide Al2O3 with nanometric size. Two variants of Ni-B/Al2O3 layers deposited from a bath containing different amounts of aluminum oxide (5 and 10 g/dm3) were prepared and for comparison purposes the Ni-B layer without built-Al2O3 particles was also studied. The powder of Al2O3 and the produced layers were examined by the scanning electron microscopy (SEM), X-Ray diffraction (XRD), optical microscopy and measurements of Vickers microhardness, and of roughness parameters of Ra and Rz. Corrosion resistance were studied by the potentiodynamic method in the environment of 0.5 M NaCl. The results of identifications of structure of the Al2O3 powder and produced Ni-B and Ni-B/Al2O3 layers, their microhardness and results of corrosion testing are presented. The produced layers are compact and have uniform thickness. Incorporation of Al2O3 powder particles in a matrix of nickel-boron increases the level of surface development and increase of corrosion resistance.

Abstract

W pracy przedstawiono wyniki badań stopowych warstw kompozytowych Ni-B/Al2O3 wytwarzanych metodą bezprądową na podłożu stalowym. Jako fazę dyspersyjną stosowano proszek tlenku glinu Al2O3 o nanometrycznych wymiarach cząstek. Wytworzono dwa warianty warstw kompozytowych Ni-B/Al2O3 osadzanych z kąpieli o różnej zawartości tlenku glinu (5 i 10 g/dm3), oraz w celach porównawczych warstwę Ni-B bez wbudowanych cząstek Al2O3. Proszek Al2O3 oraz wytworzone warstwy Ni-B badano za pomocą skaningowej mikroskopii elektronowej (SEM), dyfrakcji promieniowania rentgenowskiego (XRD), mikroskopii optycznej, pomiarów mikrotwardości metodą Vickersa oraz parametrów chropowatości Ra i Rz. Badania odporności na korozję zrealizowano metodą potencjodynamiczną w środowisku 0,5 M NaCl. Przedstawiono wyniki badań struktury proszku Al2O3 oraz powłok Ni-B oraz Ni-B/Al2O3, a także mikrotwardość oraz odporność na korozję w badanych warunkach. Wytworzone warstwy charakteryzują się zwartą budową i równomierną grubością. Wbudowanie cząstek proszku Al2O3 w niklowoborową osnowę wpływa na zwiększenie stopnia rozwinięcia powierzchni oraz zwiększenie odporności na korozję.

Słowa kluczowe

Keywords

Bibliografia

[1] Bieliński Jerzy. 1985. “Wybrane zagadnienia procesów bezprądowego osadzania warstw niklowofosforowych". Seria Chemia, Z-34. Warszawa: Wydawnictwo Politechniki Warszawskiej.
[2] Bonin L., V. Vitry. 2016. “Mechanical and wear characterization of electroless nickel mono and bilayers and high boron-mid phosphorus electroless nickel duplex coatings". Surface & Coatings Technology 307: 957-962.
[3] Bonin L., Bains N., Vitry V., Cobley A.J. 2017. “Electroless deposition of nickel-boron coatings using low frequency ultrasonic agitation: Effect of ultrasonic frequency on the coatings". Ultrasonics 77 : 61-68.
[4] Dervos C.T., J. Novakovic, P. Vassiliou. 2004. “Vacum heat treatment of electroless Ni-B coatings". Materials Letters 58 : 619-623.
[5] Hui-Long Wang, Liu Ling-Yun, Dou Yong, Zhang Wen-Zhu, Jiang Wen-Feng. 2013. “Preparation and corrosion resistance of electroless Ni-P/SiC functionally gradient coatings on AZ91D magnesium alloy", Applied Surface Science 286 : 319-327.
[6] Jagatheeshwaran M.S., A. Elayaperumal, S. Arulvel. 2015. “Wear characteristics of electroless NiP/ bio-composite coatings on En8 steel". Journal of Manufacturing Processes 20 : 206-214.
[7] Liping Wu, Yang Zhongdong, Qin Gaowu. 2017. “Kinetic study of a novel electroless Ni-P deposition on AZ91D magnesium alloy using nickel hypophosphite as the metal salt". Journal of Alloys and Compounds 694 : 1133-1139.
[8] Luo Hong, Michael Leitch, Yashar Behnamian, Yongsheng Ma, Hongbo Zeng, Jing-Li Luo. 2015. “Development of electroless Ni-P/nano-WC composite coatings and investigation on its properties". Surface & Coatings Technology 277 : 99-106.
[9] Sadeghzadeh-Attaretal A., G. AyubiKia, M. Ehteshamzadeh. 2016. “Improvement in tribological behavior of novel sol-enhanced electroless Ni-PSiO2 nanocomposite coatings". Surface & Coatings Technology 307 : 837-848.
[10] Trzaska Maria, Grzegorz Cieślak, Anna Mazurek. 2016. "Structure and properties of Ni-P/PTFE composite coatings produced by chemical reduction method". Composites: Theory and Practice 3 : 174-179.
[11] Vitry V., L. Bonin. 2017. “Increase of boron content in electroless nickel-boron coating by modification of plating conditions". Surface & Coatings Technology. 311: 164-171.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 107488 "Corrosion properties of N..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2017-7 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2017-7

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma