Precipitation of calcium carbonate from waste distillation residue and sodium bicarbonate solution in presence of disodium versenate Strącanie węglanu wapnia z płynu podestylacyjnego i roztworu wodorowęglanu sodu z metody Solvaya w obecności wersenianu disodu

10.15199/62.2016.9.9

nr katalogowy: 100764
10.15199/62.2016.9.9

CaCO3 was pptd. from the waste distn. liq. from Solvay process by addn. of satd. soln. of NaHCO3 in a lab. reactor at 20-90oC and varying dosing rate in presence of Na2 versenate and studied for bulk and packing d., cryst. structure and H2O, paraffinic oil and Bu2 phthalate absorption capacity. The addn. of Na2 versenate at 90oC resulted in an increase in the d. of CaCO3 crystals. At 90oC, the calcite and aragonite crystals were formed. At lower temps., formation of calcite crystals was also obsd. Przedstawiono wyniki badań otrzymywania węglanu wapnia z płynu podestylacyjnego DS i nasyconego roztworu wodorowęglanu sodu z metody Solvaya w obecności wersenianu disodu. Badania prowadzono w temp. 20, 50 i 90°C. Roztwory dozowano w stosunku stechiometrycznym, stosując szybkości dozowa-nia 23,6 oraz 95 cm3/min. Stosowano wersenian disodu o stężeniu 1 i 10 g/dm3 płynu DS. Dla otrzymanych prób CaCO3 oznaczano gęstość nasypową i utrząsową, chłonność wody, oleju parafinowego i ftalanu dibutylu, oraz formę krystalograficzną otrzymanych kryształów. Węglan wapnia jest jednym z najbardziej rozpowszechnionych minerałów spotykanych w przyrodzie. Występuje w wielu postaciach, z których trzy główne to kalcyt, aragonit i mniej powszechny wateryt. Węglan wapnia1) jest szeroko stosowanym surowcem w rozlicznych gałęziach przemysłu, od produkcji farb dyspersyjnych i papieru przez przetwórstwo polimerów po przemysł farmaceutyczny oraz kosmetyczny2, 3). Każda z tych rozwijających się nieustannie dziedzin przemysłu ma inne oczekiwania dotyczące właściwości CaCO3. Chemiczna czystość, powierzchnia właściwa, wielkość cząstek, chłonność wody i oleju oraz morfologia 1706 95/9(2016) determinują możliwości jego wykorzystania4). Kontrolowana synteza materiałów nieorganicznych o swoistych kształtach, rozmiarach i morfologii jest punktem wyjścia dla rozwoju nowych tworzyw sztucznych5). W związku z tym nieustannie prowadzi się prace nad modyfikacją właściwośc[...]

Bibliografia

[1] C. Combes, B. Miao, R. Bareille, C. Rey, Biomaterials 2006, 27, 1945.
[2] Q. Wei, J. Lu, H. Ai, B. Jiang, Mater. Lett. 2012, 80, 91.
[3] J. Grodzka, A. Krysztafkiewicz, T. Jesionowski, Adv. Powder Technol. 2005, 16, 181.
[4] H. Wei, Q. Shen, Y. Zhao, Y. Zhou, D. Wang, D. Xu, J. Cryst. Growth 2005, 279, 439.
[5] X. Yang, H. Meng, T. Li, L. Shi, Y. Li, G. Xu, Powder Technol. 2014, 256, 272.
[6] L. He, R. Xue, R. Song, J. Solid State Chem. 2009, 182, 1082.
[7] M. Trypuć, K. Białowicz, J. Clean. Prod. 2011, 19, 751.
[8] K. Białowicz, M. Trypuć, U. Kiełkowska, Przem. Chem. 2010, 89, nr 1, 72
[9] P. Liang, Y. Zhao, Q. Shen, D. Wang, D. Xu, J. Cryst. Growth 2004, 261, 571.
[10] N. Wada, S. Suda, K. Kanamura, T. Umegaki, J. Colloid Interf. Sci. 2004, 279, 167.
[11] F. Zhang, J. Wang, Z. Hou, M. Yu, L. Xie, Mater. Design 2006, 27, 422.
[12] A. Ulčinas, M.F. Butler, M. Heppenstall-Butler, S. Singleton, M.J. Miles, J. Cryst. Growth 2007, 307, 378.
[13] K. Białowicz, Przem. Chem. 2010, 89, nr 1, 77.
[14] K. Białowicz, M. Trypuć, Przem. Chem. 2011, 90, nr 1, 148.
[15] K.J. Westin, Å.C. Rasmuson, J. Colloid Interf. Sci. 2005, 282, 359.
[16] E. Altay, T. Shahwan, M. Tanoglu, Powder Technol. 2007, 178, 194.
[17] K.J. Westin, Å.C. Rasmuson, J. Colloid Interf. Sci. 2005, 282, 370.
[18] Shanmukha Prasid Gopi, V.K. Subramanian, Desalination 2012, 297, 38.

Zeszyt


PRZEGLĄD ELEKTROTECHNICZNY - e-zeszyt (pdf) 2008-7 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEGLĄD ELEKTROTECHNICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEGLĄD ELEKTROTECHNICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEGLĄD ELEKTROTECHNICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Open Access

Zeszyt

2016-9

Twój Koszyk

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma