Czasopismo | PRZEMYSŁ CHEMICZNY | Rocznik 2017 - zeszyt 5

Studies on temperature changes during polymerization of light-cured dental composite materials Badanie zmian temperatury podczas polimeryzacji światłoutwardzalnych dentystycznych materiałów kompozytowych

10.15199/62.2017.5.40

nr katalogowy: 105752
10.15199/62.2017.5.40

Two com. resin-based composites with silorane-and methacrylate-based matrices were photocured at varying light-curing unit and composite type, curing distance and curing time to obs. the temp. changes. The silorane-based composite was cured at significantly higher temp. when compared with the methacrylate-based one. The curing time showed a stronger effect on temp. changes when the light-emitting diode was used as the light source than when halogen lamp was used. Przeprowadzono badania zmian temperatury podczas polimeryzacji dwóch materiałów kompozytowych o różnych matrycach (siloranowej i metakrylanowej) w zależności od rodzaju zastosowanej lampy polimeryzacyjnej, odległości od źródła światła i czasu naświetlania. Temperatura podczas naświetlania materiału Filtek Silorane o matrycy siloranowej była istotnie wyższa od temperatury materiału Filtek P60 o matrycy metakrylanowej. Zaobserwowano też istotnie większy wpływ czasu naświetlania na zmiany temperatury podczas naświetlania lampami LED (light-emitting diodes) niż lampą halogenową. Wśród czynników wpływających na przebieg procesu polimeryzacji znajdują się parametry pośrednio związane z rodzajem materiału kompozytowego, takie jak odcień, grubość utwardzanej warstwy oraz skład samego materiału. Natężenie i długość fali światła, czas naświetlania, wielkość i położenie oraz kierunek końcówki źródła światła to czynniki związane z lampami polimeryzacyjnymi1). Lampy polimeryzacyjne podczas naświetlania mogą powodować wzrost temperatury, który może prowadzić do nieodwracalnego uszkodzenia miazgi zęba1, 2). Ryzyko uszkodzenia miazgi zęba wywołanego wzrostem temperatury podczas polimeryzacji wypełnień stomatologicznych jest obiektem badań od wielu lat. Na związane ze wzrostem temperatury niekorzystne zmiany w miazdze zęba mają wpływ takie czynniki, jak odcień i grubość utwardzanej warstwy materiału kompozytowego, jego skład i porowatość3), a także czas naświetlania i grubość zębi[...]

Bibliografia

[1] Y.H. Kwon, T.Y. Kwon, J.L. Ong, K.H. Kim, J. Prosthet. Dent. 2002, 88, 396.
[2] A.U. Yap, M.S. Soh, Oper. Dent. 2003, 28, 260.
[3] Z. Czech, A. Butwin, J. Kabatc, J. Świderska, Polym. Bull. 2012, 68, 441.
[4] E. Asmussen, A. Peutzfeldt, Eur. J. Oral Sci. 2005, 113, nr 1, 96.
[5] F.H. Aguiar, G.K. Barros, A.J. dos Santos i in., Oper. Dent. 2005, 30, 602.
[6] J. Leprince, J. Devaux, T. Mullier i in., Oper. Dent. 2010, 35, nr 2, 220.
[7] D.A. Stewardson, A.C.C. Shortall, E. Harrington, P.J. Lumley, J. Dent. 2004, 32, nr 8, 643.
[8] A.Uhl, R.W. Mills, K.D. Jandt, Biomaterials 2003, 24, nr 10, 1809.
[9] W. Świderski, Z. Czech, P. Malara, Przem. Chem. 2014, 93, nr 12, 2214.
[10] Z. Czech, A. Kowalczyk, J. Kabatc, J. Świderska, Eur. Polym. J. 2012, 48, 1446.
[11] G. Chladek, K. Basa, J. Żmudzki, P. Malara i in., Acta Bioeng. Biomech. 2016, 18, nr 3, 43.
[12] E. Asmussen, A. Peutzfeldt, Quintessence Int. 2003, 34, 1.
[13] W.J. Dunn, A.C. Bush, J. Am. Dent. Assoc. 2002, 133, 335.
[14] R.W. Mills, A.Uhl, G.B. Blackwell, K.D. Jandt, Biomaterials 2002, 23, 2955.
[15] C. Besnault, N. Pradelle-Plasse, B. Picard, P. Colon, Am. J. Dent. 2003, 16, 323.
[16] A.V. Rajesh Ebenezar, R. Anilkumar, R. Indira i in., J. Conserv. Dent. 2010, 13, 132.
[17] I. Hubbezoglu, A. Dogan, O.M. Dogan i in., Dent. Mater. J. 2008, 27, nr 4, 581.
[18] P. Malara, A. Fischer, B. Malara, J. Occup. Med. Toxicol. 2016, 11, 56.
[19] R.D. Guiraldo, S. Consani, R.L. Consani i in., Braz. Dent. J. 2013, 24, nr 3, 258.
[20] V. Miletic, V. Ivanovic, B. Dzeletovic, M. Lezaja, J. Esthet. Restor. Dent. 2009, 21, nr 2, 122.
[21] B. Ozturk, A.N. Ozturk, A. Usumez i in., Oper. Dent. 2004, 29, 325.
[22] Z. Tarle, A. Meniga, A. Knezević i in., J. Oral. Rehabil. 2002, 29, 662.
[23] R. Nomoto, J.F. McCabe, S.Hirano, Oper. Dent. 2004, 29, 287.
[24] R.B. Price, L. Ehrnford, P. Andreou, C.A. Felix, J. Adhes. Dent. 2003, 5, 193.

Zeszyt


PRZEMYSŁ CHEMICZNY - e-zeszyt (pdf) 2017-5 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEMYSŁ CHEMICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEMYSŁ CHEMICZNY - prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEMYSŁ CHEMICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Open Access

Zeszyt

2017-5

Twój Koszyk

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma