Electrochemical impedance spectroscopy of Ni-Mo alloy coatings in 0.5 M NaCl solution

10.15199/40.2017.4.2

nr katalogowy: 105015
10.15199/40.2017.4.2

The corrosion resistance of Ni-Mo (11÷32 wt% Mo) alloy coatings during 72 h exposure in 0.5 mol·dm-3 solution of NaCl was investigated by means of EIS method. The highest corrosion resistance (charge transfer resistance >12 kΩ·cm2) among all investigated coatings was measured for Ni-Mo coatings with higher molybdenum content (21÷32 wt%). However, after 48-60 h of immersion, visible micro cracks appeared in Ni-28 wt% Mo and Ni-32 wt% Mo alloy coatings, probably due to the significant internal stresses. This phenomenon was observed especially for Ni-32 wt% Mo coating, and it was accompanied by an abrupt decrease in a charge transfer resistance from 8.7 to 2.7 kΩ·cm2 after 5 and 24 h, respectively. According to EIS results, coating containing 21 wt% Mo offers the best protective properties towards steel substrate. This may be associated with the existence of a compact, tight and very thin passive layer which does not undergo damage during exposure. Keywords: Ni-Mo coating; passive layer; electroplating, SEM, EIS Metodą EIS zbadano odporność na korozję powłok Ni-Mo (11÷32% mas. Mo) w czasie 72 h ekspozycji w 0,5 mol·dm-3 roztworze NaCl. Najwyższą odpornością na korozję (rezystancja przeniesienia ładunku >12 kΩ·cm2), spośród wszystkich zbadanych powłok, charakteryzowały się powłoki Ni-Mo o zawartości 21÷32% mas. molibdenu. Zauważono jednak, że po 36÷60 h ekspozycji, na powierzchni powłok Ni-28% mas. Mo oraz Ni-32% mas. Mo pojawiły się widoczne pęknięcia, których przyczyną są najprawdopodobniej duże naprężenia wewnątrz powłok. To zjawisko było szczególnie wyraźne w przypadku powłoki Ni-32% mas. Mo, bowiem towarzyszył mu gwałtowny spadek rezystancji przeniesienia ładunku z 8,7 do 2,7 kΩ·cm2 po odpowiednio 5 i 24 h ekspozycji. Zgodnie z wynikami pomiarów metodą EIS, powłoka Ni-Mo zawierająca 21% mas. Mo zapewnia najlepsze właściwości ochronne podłoża stalowego, pomimo nieznacznie niższej[...]

Bibliografia

[1] Alireza Akbari, Farzad Nasirpouri, Mir Ghasem Hosseini. 2014. “Corrosion resistance of Ni-Co alloy and Ni-Co/SiC nanocomposite coatings electrodeposited by sediment codeposition technique". Appl Surf Sci 307 : 351-359.
[2] Bełtowska-Lehman Ewa, Agnieszka Bigos, Paulina Indyka, Marcin Kot. 2012. “Electrodeposition and characterization of nanocrystalline Ni-Mo coatings". Surf Coat Technol 211 : 67-71.
[3] Hashimoto Kenkichi, Kenichi Asami, A. Kawashima, Hiroki Habazaki, Eiji Akiyama. 2007. “The role of corrosion-resistant alloying elements in passivity". Corros Sci 49 : 42-45.
[4] Hirschorn Bryan, Mark E. Orazem, Bernard Tribollet, Vincent Vivier, Isabelle Frateur, Marco Musiani. 2010. “Determination of effective capacitance and film thickness from constant-phase-element parameters". Electrochim Acta 55 : 6218-6227.
[5] Huang Pao-Chang, Kung-Hsu Hou, Hung-Hua Sheu, Ming-Der Ger, Gao-Liang Wang. 2014. “Wear properties of Ni-Mo coatings produced by pulse electroforming". Surf Coat Technol 258 : 639-645.
[6] Orazem Mark E., Isabelle Frateur, Bernard Tribollet, Vincent Vivier, Sabrina Marcelin, Nadine Pebere, Annette L. Bunge, Erick A. White, Douglas P. Riemer, Marco Musiani. 2013. “Dielectric Properties of Materials Showing Constant- Phase-Element (CPE) Impedance Response". J. Electrochem Soc 160 (6) : C215- C225.
[7] Park P.Y., Eiji Akiyama, A. Kawashima, Kenichi Asami, Kenkichi Hashimoto. 1996. “The corrosion behavior of sputter-deposited Mo-Ta alloys in 12 M HCl solution". Corros Sci 38 : 397-411.
[8] Srivastava Meenu, C. Anandan, V.K. William Grips. 2013. “Ni-Mo-Co ternary alloy as replacement for hard chrome". Appl Surf Sci 285P : 167-174.
[9] Szczygieł Bogdan, Agnieszka Laszczyńska. 2014. “Influence of bath concentration and pH on electrodeposition process of ternary Zn-Ni-Mo alloy coatings". Trans Inst Met Finish 92 : 196-202.
[10] Szczygieł Bogdan, Agnieszka Laszczyńska, Włodzimierz Tylus. 2010. “Influence of molybdenum on properties of Zn-Ni and Zn-Co alloy coatings". Surf Coat Technol 204 : 1438-1444.
[11] Winiarski Juliusz, Włodzimierz Tylus, Katarzyna Winiarska, Bogdan Szczygieł. 2015. “The influence of molybdenum on the corrosion resistance of ternary Zn-Co-Mo alloy coatings deposited from citrate-sulphate bath". Corros Sci 91 : 330-340. Acknowledgements The work was co-financed by statutory activity subsidy from the Polish Ministry of Science and Higher Education for the Faculty of Engineering and Economics of Wrocław University of Economics (Department of Inorganic Chemistry) and for the Faculty of Chemistry of Wrocław University of Science and Technology (Department of Advanced Material Technologies - grant number 0401/0262/16).

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 105015 "Electrochemical impedance..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2017-4 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2017-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma