The influence of aging process parameters on selected mechanical properties of profiles from EN AW-6106 aluminium alloy

10.15199/24.2017.1.17

nr katalogowy: 103558
10.15199/24.2017.1.17

The aim of this article was to analyze the influence of temperature and time period of artificially aging process on selected mechanical properties: Brinell hardness, yield strength, tensile strength, and elongation of hot extruded profiles from EN AW-6106 aluminum alloy. The result of the conducted research has pointed out that the temperature and the time of aging process had a significant effect on the selected mechanical properties. In the study it was found that the highest mechanical properties such as the yield strength and tensile strength for analyzed aluminum alloy were achieved for samples aged in temperature of 165°C for time period of 6 hours. The value of mechanical properties required be the standards for T6 temper were achieved after 2 hours of artificial aging in temperature of 165°C.1. Introduction. One of most important step in the production of aluminum profiles is their precipitation hardening made by heat treatment processes, which are supersaturation and aging. The first heat treatment operation in aluminium profiles production is supersaturation of extrudate which is conducted at the press exit. Supersaturation is carried out in temperatures above the solvus temperature for the particular alloy, wherein the alloying elements can be completely dissolved, held in elevated temperature and then rapidly cooled up to ambient temperature to retain the alloying elements in the supersaturated solid solution. This heat treatment process decreases mechanical properties and increases plastic properties [1-3, 16]. The second heat treatment operation of hot extruded aluminium profiles is aging process. In aging process precipitate from supersaturated solid solution the phase (or phases) of appropriate dispersion containing an alloying component, present in solution in excess. If the precipitation occurs under the influence of diffusion in room temperature, then such a process is called naturally aging. However, the[...]

Bibliografia

[1] Dobrzański Leszek. A. 2006. Podstawy nauki o materiałach i metaloznawstwo. Warszawa: Wydawnictwo Naukowo Techniczne.
[2] Goryckiewicz Ryszard. 2003. "Wpływ twardości i mikrostruktury stopów aluminium na udarność". Archiwum Odlewnictwa 8: 279-286. Katowice: Polish Academy of Sciences.
[3] Kawecki Artur. 2013. Wysoko wytrzymałe stopy Cu-Ag o wysokiej przewodności elektrycznej. Kraków: Wydawnictwo: Wzorek.
[4] Mróz Sebastian, Szota Piotr, Stefanik Andrzej,Wąsek Seweryn, Stradomski Grzegorz. 2015. ��Analysis of Al-Cu bimetalic bars properties after explosive welding and rolling in modified passes. Archives of Metallurgy and Materials Volume 60, Issue 1: 427-432.
[5] Podręcznik konstruktora. 1997. Jak radzić sobie z profilami aluminiowymi. Trzcianka: Dział Marketingu SAPA. Fig. 5. Elongation graph Rys. 5. Wykres wydłużenia Fig. 5. Exemplary microstructure of profile from EN AW-6106 aluminium alloy Rys. 5. Przykładowa mikrostruktura profile ze stopu aluminium EN AW-6106 s. 65 HUTNIK-WIADOMOŚCI HUTNICZE Nr 1
[6] PN-EN 573-3:2014-0��2. 2014. Aluminium and aluminium alloys - Chemical composition and form of wrought products - Part 3: Chemical composition and form of products. Warszawa: Polski Komitet Normatyzacyjny.
[7] PN-EN ISO 6892-1:2016, Metale Metallic materials - Tensile testing - Part 1: Method of test at room temperature, Polski Komitet Normatyzacyjny, Warszawa.
[8]
[PN-EN ISO 6506-1:2014-12. 2014. Metallic materials - Brinell hardness test - Part 1: Test method. Warszawa: Polski Komitet Normatyzacyjny.
[9] PN-EN 755-2:2016, Aluminium Aluminium and aluminium alloys. ��Extruded rod/bar, tube and profiles - Part 2: Mechanical properties, Polski Komitet Normatyzacyjny, Warszawa 2010.
[10] Richert Jan. 2010. Innowacyjne metody przeróbki plastycznej metali. Kraków: Wydawnictwo AGH.
[11] Richert Jan, Mroczkowski Marcin, Gellner Jerzy. 2006. "Nowy sposób starzenia stopów AlMgSi wyciskanych w stanie T5". Rudy i Metale Nieżelazne Nr 12: 747-753. Warszawa: Sigma-NOT.
[12] Richert Jan, Woźnicka Agata. 2013. "Przeróbka plastyczna trudno odkształcalnych stopów aluminium zintegrowana z przesycaniem". Rudy i Metale Nieżelazne Nr 2: 90-95. Warszawa: Sigma-NOT.
[13] Romański Piotr, Adamczyk Justyna, Pilarczyk Jan Walenty. 2014. "The influence of temperature and time period of ageing process of extruded aluminium profiles from 6063 alloy on the selected mechanical properties". XV International Scientific Conference - New Technologies and Achievements in Metallurgy and Material Engineering and Production Engineering, Monografia Nr 40: 150-155. ��Częstochowa: Wydawnictwo Wydziału Inżynierii Produkcji i Technologii Materiałów Politechniki Częstochowskiej.
[14] Romański Piotr, Stradomski Grzegorz, Ciepiela Wojciech, Pilarczyk Jan Walenty. ��2015. "The influence of heat treatment on toughness of extruded profiles from EN AW-6060 aluminium alloy", Hutnik Wiadomości Hutnicze Nr 1: 101-104. Warszawa: Sigma-NOT.
[15] Romański Piotr, Stradomski Grzegorz, Pilarczyk Jan Walenty. 2016. "The influence of heat treatment on toughness of extruded profiles from EN AW - 6063 aluminium alloy", Hutnik-Wiadomości Hutnicze 5: 223-227.
[16] Wendland Justyna, Borowski Jacek, Jurczak Henryk. 2014. "Matryce do wyciskania profili aluminiowych i sposoby ich umacniania". Projektowanie I Konstrukcje Inżynierskie 4. Warszawa: Wydawnictwo: ITER.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 103558 "The influence of aging pr..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


HUTNIK - WIADOMOŚCI HUTNICZE - e-zeszyt (pdf) 2017-1 licencja: Osobista Produkt cyfrowy	32.00 zł
HUTNIK - WIADOMOŚCI HUTNICZE - e-zeszyt (pdf) 2017-10 licencja: Osobista Produkt cyfrowy	32.00 zł
HUTNIK - WIADOMOŚCI HUTNICZE - e-zeszyt (pdf) 2017-11 licencja: Osobista Produkt cyfrowy	32.00 zł
HUTNIK - WIADOMOŚCI HUTNICZE - e-zeszyt (pdf) 2017-12 licencja: Osobista Produkt cyfrowy	32.00 zł

Prenumerata

HUTNIK - WIADOMOŚCI HUTNICZE - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

400.00 zł

HUTNIK - WIADOMOŚCI HUTNICZE - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
HUTNIK - WIADOMOŚCI HUTNICZE - papierowa prenumerata roczna	540.00 zł brutto 500.00 zł netto 40.00 zł VAT (stawka VAT 8%)
HUTNIK - WIADOMOŚCI HUTNICZE - pakowanie i wysyłka	14.00 zł brutto 11.38 zł netto 2.62 zł VAT (stawka VAT 23%)

554.00 zł

HUTNIK - WIADOMOŚCI HUTNICZE - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
HUTNIK - WIADOMOŚCI HUTNICZE - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2017-1

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma