Czasopismo | INŻYNIERIA MATERIAŁOWA | Rocznik 2016 - zeszyt 5

The influence of heating rate during sintering on mechanical properties of Fe40Al sinters at room temperature

10.15199/28.2016.5.11

nr katalogowy: 101858
10.15199/28.2016.5.11

The results of a uniaxial compression test of Fe40Al (at. %) sintered powders are presented. Compression yield stress Rc0.2, ultimate strength Rcm, permanent deformation, and true compression strength at the maximum force point were determined. All Fe40Al sinters behaved like a plastic material; they were not brittle, and the sample after the compression test did not fall apart and was barrel-shaped. Observations of the microstructure revealed plastically-deformed grains. The obtained sinters were characterized by very high ultimate compressive strength (ok. 2700÷2800 MPa) and low yield stress (Rc0.2 approx. 280 MPa). This paper presents also XRD analyses, microstructure, and density of Fe40Al sinters. Key words: intermetallic alloys, iron aluminides, reaction synthesis, compression test, plasticity.1. INTRODUCTION Despite its obvious advantages, such as low density, good corrosion and oxidation resistance, and high strength at both room and elevated temperature [1÷3], the FeAl-based alloys are still only potentially used as replacements for expensive alloy steels; this is primarily due to their ductility and inherently low toughness, especially at ambient temperature [4]. It is generally known that the mechanical properties of iron aluminides are very sensitive to many factors, including aluminium content, order, heat treatment, the test temperature, alloying additions, environment, microstructure, and defects [5]. Due to the fragility of Fe-Al alloys, which increases with increasing aluminium content, alloys with an aluminium content of 40% are the most frequently analysed. FeAl alloys of 40% Al are characterized by high strength properties at an acceptable ductility. Due to the potential embrittlement of sintered FeAl powders, it is tested mostly by the compression test. Literature sources indicate that the yield stress of Fe40Al at ambient temperature ranges from 380 to 820 MPa [4, 6÷9]. The strain obtained during testing strength[...]

Bibliografia

[1] Grosdidier T. Ji. G., Bernard F., Gaffet E., Munir Z. A., Launois S.: Synthesis of bulk FeAl nanostructured materials by HVOF spray forming and spark plasma sintering. Intermetallics 14 (2006) 1208÷1213.
[2] Godlewska E., Szczepanik S., Mania R., Krawiarz J., Kozinski S.: FeAl materials from intermetallic powders. Intermetallics 11 (2003) 307÷312.
[3] Martinez M., Viguier B., Maugis P., Lacaze J.: Relation between composition, microstructure and oxidation in iron aluminides. Intermetallics 14 (2006) 1214÷1220.
[4] Deevi S. C., Sikka V. K.: Nickel and iron aluminides: An overview on properties, processing, and applications. Intermetallics 4 (1996) 357÷375.
[5] Physical metallurgy and processing of intertnetallic compounds. Edited by N. S. Stoloff, V. K. Sikka, Chapman&Hall (1996) 361.
[6] Kupka M.: Can vacancies be the main reason of FeAl alloys hardening? Journal of Alloys and Compounds 437 (2007) 373÷377.
[7] Skiba T., Hausild P., Karlí M., Vanmeensel K., Vleugels J.: Mechanical properties of spark plasma sintered FeAl intermetallics. Intermetallics 18 (2010) 1410÷1414.
[8] Łyszkowski R., Bystrzycki J.: Hot deformation and processing maps of a Fe-Al intermetallic alloy. Materials Characterization 96 (2014) 196÷205.
[9] Karczewski K., Józwiak S., Bojar Z.: Mechanisms of strength properties anomaly of Fe-Al sinters by compression tests at elevated temperature. Archives of metallurgy and materials 52 (2007) 361÷366.
[10] Sundar R. S., Baligidad R. G., Prasad Y. V. R. K., Sastry D. H.: Processing of iron aluminides. Materials Science and Engineering A258 (1998) 219÷228.
[11] Yang Y., Baker I.: The influence of vacancy concentration on the mechanical behavior of Fe40Al. Intermetallics 6 (1998) 167÷175.
[12] Xiao H., Baker I.: The relationship between point defects and mechanical properties in Fe-Al at room temperature. Acta Metall. Mater. 43 (1995) 391÷396.
[13] Siemiaszko D., Mościcki R.: Kinetics study on the SHS reaction in massive samples with high heating rate in the Fe-Al system. J. of Alloys and Compound 632 (2015) 335÷342.
[14] Siemiaszko D., Kowalska B., Jóźwik P., Kwiatkowska M.: The effect of oxygen partial pressure on microstructure and properties of Fe40Al alloy sintered under vacuum. Materials 8 (2015) 1513÷1525.
[15] Lynch R. J., Heldt L. A.: Effects of annealing temperature on the mechanical properties of an Fe-36% Al alloy. Scripta Metallurgica et Materialia 30 (1994) 895÷898.
[16] Klein O., Baker I.: Effect of heat-treatment on the tensile behavior of iron-rich FeAl and FeAl + B. Scripta Metallurgica et Materialia 30 (1994) 627÷632.
[17] Nagpal P., Baker I.: Effect of cooling rate on hardness of FeAl and NiAl. Metallurgical Transactions A 21A (1990) 2281÷2282.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 101858 "The influence of heating ..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


INŻYNIERIA MATERIAŁOWA - e-zeszyt (pdf) 2016-5 licencja: Osobista Produkt cyfrowy	65.00 zł

Prenumerata

INŻYNIERIA MATERIAŁOWA - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

402.00 zł

INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - papierowa prenumerata roczna	492.00 zł brutto 455.56 zł netto 36.44 zł VAT (stawka VAT 8%)
INŻYNIERIA MATERIAŁOWA - pakowanie i wysyłka	21.00 zł brutto 17.07 zł netto 3.93 zł VAT (stawka VAT 23%)

513.00 zł

INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
INŻYNIERIA MATERIAŁOWA - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	600.00 zł brutto 555.56 zł netto 44.44 zł VAT (stawka VAT 8%)

600.00 zł

Zeszyt

2016-5

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma