Synthesis and mechanical properties of epoxy-polyurethane materials filled with sepiolite Synteza i właściwości mechaniczne materiałów epoksydowo-poliuretanowych napełnianych sepiolitem

10.15199/62.2016.10.40

nr katalogowy: 101533
10.15199/62.2016.10.40

Oxirane rings in epoxidized soybean oil were opened in reaction with monoethylene glycol and then fused with bisphenol A, hydroxylated soybean oil and a com. low-mol.- mass epoxy resin in bulk. The polymeric products were filled with sepiolite (1 or 2% by mass) and crosslinked with a 4,4’-diphenylmethane diisocyanate. The composite materials produced were studied for static tensile, flexural and compression strength, impact resistance, hardness and resilience as well as for thermal stability and morphol. The addn. of sepiolite resulted in a decrease in mech. strength and thermal stability of the composites. Otrzymano i zbadano właściwości mechaniczne kompozycji epoksydowo-poliuretanowych na bazie epoksydowanego i hydroksylowanego oleju sojowego oraz sepiolitu. W pierwszym etapie przeprowadzono reakcję otwarcia pierścieni oksiranowych w epoksydowanym oleju sojowym przy użyciu glikolu monoetylenowego, otrzymując hydroksylowany olej sojowy. Epoksydową i hydroksylową pochodną oleju sojowego wykorzystano w procesie stapiania z bisfenolem A oraz z małocząsteczkową dianową żywicą epoksydową EPR 162. Scharakteryzowano otrzymane produkty oraz opracowano metodę wprowadzania sepiolitu do kompozycji epoksydowych. Produkty stapiania usieciowano 4,4’-diizocyjanianem difenylometanu. Zbadano właściwości mechaniczne (wytrzymałość na rozciąganie, zginanie i ściskanie, twardość Shore’a, udarność wg Charpy᾿ego i odbojność), jak również właściwości termiczne i morfologię otrzymanych nanokompozycji. Żywice epoksydowe są jednymi z istotniejszych materiałów polimerowych, które z uwagi na swoje bardzo dobre właściwości użytkowe, takie jak m.in. duża wytrzymałość mechaniczna, duża odporność cieplna i chemiczna, mała chłonność wody, dobra adhezja do podłoża i bardzo dobre właściwości dielektryczne1, 2), znalazły zastosowanie w różnych dziedzinach przemysłu oraz życia codziennego. W związku z koniecznością poszukiwania alt[...]

Bibliografia

[1] P. Czub, Modyfikowane oleje roślinne oraz produkty degradacji odpadowego poli(tereftalanu etylenu) jako ekologiczne surowce do żywic epoksydowych, Wydawnictwo PK, Kraków 2008.
[2] P. Czub, Z. Bończa-Tomaszewski, P. Penczek, J. Pielichowski, Chemia i technologia żywic epoksydowych, WNT, Warszawa 2002.
[3] J. Zhu, K. Chandrashekhara, V. Flanigan, K. Shubhender, J. Appl. Polymer Sci. 2004, 91, nr 6, 3513.
[4] P. Czub, P. Kasza, Polimery 2014, 59, nr 6, 466.
[5] N. Volle, F. Giulieri, A. Burr, S. Pagnotta, A.M. Chaze, Mater. Chem. Phys. 2012, 134, 417.
[6] Y. Yu, S. Qi, J. Zhan, Z. Wu, X. Yang, D. Wu, Mater. Research Bull. 2011, 46, 1593.
[7] L. Bokobza, A. Burr, G. Garnaud, M.Y. Perrin, S. Pagnotta, Polymers Intern. 2004, 53, 1060.
[8] S.O. Ilyin, T.V. Brantseva, I.Yu. Gorbunova, S.V. Antonov, M.Yu.M. Korolev, M.L. Kerber, Intern. J. Adhesion Adhesives 2015, 61, 127.
[9] A. Zotti, A. Borriello, A. Martone, V. Antonucci, M. Giordano, M. Zarrelli, Composites Part B: Engineering 2014, 67, 400.
[10] H. Zhang, L.C. Tang, Z. Zhang, K. Friedrich, S. Sprenger, Polymer 2008, 49, 3816.
[11] C.H. Chen, J.Y. Jian, F.S. Yen, Composites Part A: Appl. Sci. Manuf. 2009, 40, 463.
[12] N.T. Phong, M.H. Gabr, K. Okubo, B. Chuong, T. Fujii, Mater. Design 2013, 47, 624.
[13] A. Zotti, A. Borriello, A. Martone, V. Antonucci, M. Giordano, M. Zarrelli, Composites Part B: Engineering 2014, 67, 400.
[14] PN-87/C-89085/13, Żywice epoksydowe nieutwardzone. Metody badań.
[15] PN-93/C-89052/03, Polietery do poliuretanów. Metody badań. Oznaczanie liczby hydroksylowej.
[16] PN-EN ISO 527-1:2012, Tworzywa sztuczne. Oznaczanie właściwości mechanicznych przy statycznym rozciąganiu. Warunki badań folii i płyt.
[17] PN-EN ISO 178:2011, Tworzywa sztuczne. Oznaczanie właściwości przy zginaniu.
[18] PN-EN ISO 604:2006, Tworzywa sztuczne. Oznaczanie właściwości przy ściskaniu.
[19] PN-EN ISO 179-2:2001, Tworzywa sztuczne. Oznaczanie udarności metodą Charpy’ego. Instrumentalne badanie udarności.
[20] PN-EN ISO 868:2005, Tworzywa sztuczne i ebonit. Oznaczanie twardości metodą wciskania z zastosowaniem twardościomierza (twardość metodą Shore’a).

Zeszyt


PRZEMYSŁ CHEMICZNY - e-zeszyt (pdf) 2016-10 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEMYSŁ CHEMICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEMYSŁ CHEMICZNY - prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEMYSŁ CHEMICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Open Access

Zeszyt

2016-10

Twój Koszyk

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma