Metallization of glass optic fibers by a combined chemical-electrochemical method Metalizacja włókien światłowodowych metodą chemiczno-elektrochemiczną

10.15199/62.2016.8.40

nr katalogowy: 100403
10.15199/62.2016.8.40

Com. acrylics-coated, optical glass fibers were washed with Me2NCH, degreased with a NaOH soln., etched with HF, activated by chem. coating with Ag (redn. of Ag+ with Sn2+), chem. (current less) plated with Cu and then electroplated with Cu (up to 1 A/dm2) for 15 min. Optionally, the Cu-coated fibers were addnl. chem. plated with Ni. The Nicoated fibers were more heat resistant than the Cu-coated ones. The coating with Cu resulted in an increase of the tensile strength of the fiber. The metal-plated fibers were successively soldered with a soft Sn-Pb solder. Surface quality was assessed by optical microscopy. Opracowano wieloetapową chemiczno-elektrochemiczną metodę metalizacji włókien światłowodowych miedzią i niklem bez etapu aktywacji palladem. Metoda obejmuje odtłuszczanie, trawienie, uczulanie, aktywację, metalizację chemiczną i metalizację elektrochemiczną. Podano wyniki testów wytrzymałościowych oraz przykład zastosowania otrzymanych metalizowanych włókien. W ostatnich dekadach nastąpił dynamiczny rozwój i wdrażanie systemów światłowodowych w wielu dziedzinach inżynierii, nauki i techniki. Pierwsze zastosowanie na dużą skalę światłowody znalazły w systemach telekomunikacyjnych, a obecnie produkuje się ponad 200 mln km włókien światłowodowych rocznie1). Wykorzystuje się je także w metrologii i medycynie oraz jako element sensorów2- 7). Zainteresowanie zintegrowaną optyką wynika z licznych zalet systemów światłowodowych, m.in. dużej przepustowości przy niskich parametrach tłumienia (0,17 dB/km) w paśmie fal o długości 1550 nm1), małego zużycia mocy, małych wymiarów i masy, zdecydowanie większej niezawodności i mniejszego nakładu kosztów niż w przypadku kabli metalowych8). W technice światłowodowej podstawowym materiałem jest włókno światłowodowe. Składa się ono z dwóch warstw szkła kwarcowego SiO2 o różnych współczynnikach załamania światła (rys. 1). Wewnętrzna warstwa włókna to tzw. rdzeń o współczynniku załamania n1[...]

Bibliografia

[1] K. Schuster, S. Unger, C. Aichele, F. Lindner, S. Grimm, D. Litzkendorf, J. Kobelke, J. Bierlich, K. Wondraczek, H. Bartelt, Adv. Opt. Techn. 2014, 3, nr 4, 447.
[2] P. Sanecki K. Gibała, P. Skitał, IEEE Sensors J. 2015, 15, 1275.
[3] T. Stanczyk, K. Wysokinski, T. Tenderenda, S. Lipinski, L. Ostrowski, M. Broczkowska, A. Ziolowicz, K. Gibala, H. Krisch, B. Niermann, L. Jaroszewicz, T. Nasilowski, Mat. 23rd Int. Conf. on Optical Fiber Sensors OFS-23, 2-6.06.2014, Santander (Hiszpania), Proc. SPIE 2014, 9157, 9157.
[4] T. Yoshino, K. Kurosawa, K. Itoh, T. Ose, IEEE J. Quantum Electronics 1982, 18, nr 10, 1624.
[5] K.T.V. Grattan, B.T. Meggitt (red.), Optical fiber sensor technology, Chapman & Hall, London 1995.
[6] K.T.V. Grattan, B.T. Meggitt (red.), Optical fiber sensor technology, t. 2 Devices and technology, Springer-Verlag, Berlin 1998.
[7] N. Fernandes, K. Gossner and H. Krisch, Mat. SPIE 4th Eur. Workshop Opt. Fiber Sens., 2010, 7653, 765328, doi: 10.1117/12.866621.
[8] M. Bass, E.W. Van Stryland, D.R . Williams, W.L. Wolfe, Handbook of optic. Devices, measurements and properties, t. 2, R.R. Donnelly & Sons Company, USA 1995.
[9] M. Szustakowski, Elementy techniki światłowodowej, WNT, Warszawa 1992.
[10] K. Schuster, J. Kobelke, K. Rose, M. Helbig, M. Zoheidi, A. Heinze, Mat. SPIE 7598, Optical Components and Materials VII, 75980H, 2010.
[11] K. Perlicki, Pomiary w optycznych systemach telekomunikacyjnych, WKŁ, Warszawa 2002.
[12] V.A. Bogatyrev, S. Semjonov,
[w:] Specialty optical fibers handbook (red. A. Méndez, T.F Morse), Academic Press Elsevier, 2007, 491-512.
[13] Wei Sua, Libei Yaoa, Fang Yanga, Peiyuan Li, Juan Chena, Lifang Lianga, Appl. Surface Sci. 2011, 257, 8067.
[14] M. Charbonnier, M. Romand, Surface Coatings Technol. 2002, 162,19.
[15] Wan-Fu Liena, Po-Chen Huangb, Shi-Chang Tsengc, Chia- Hsiang Chengb, Shih-Ming Lai b,Wen-Chang Liawb, Appl. Surface Sci. 2012, 258, 2246.
[16] Qiuyu Zhang, Min Wu1, Wen Zhao, Surface Coatings Technol. 2005, 192, 213.
[17] Farid Hanna, Z. Abdel Hamid, A. Abdel Aal, Materials Lett. 2003, 58, 104.
[18] T.J. Peret, Pat. USA 7158708 B2 (2007).
[19] M.E. Ives, Jr., Th.W. Engel, Pat. USA 6753034 B2 (2004).
[20] M.N. Miller, Pat. USA 6355301 B1 (2002).
[21] M.S. Chen, Pat. USA 6251252 B1 (2001).
[22] Yulong Li, Zhang Hua, Feng Yan, Peng Gang, Opt. Fiber Technol. 2009, 15, 391.
[23] M.N. Miller, Pat. świat. WO2002036852 A2 (2002).
[24] J.C.W. Kruishoop, P.E.J. Legierse, J. Van Ruler, D.J. Broer, Pat. USA 4609437 A (1986).
[25] N. Fritz, H.-C. Koo, Z. Wilson, E. Uzunlar, Z. Wen, X. Yeow, S.A. Bidstrup Allen, P.A. Kohl, J. Electrochem. Soc. 2012, 159, D386.
[26] J. Supniewski, Preparatyka nieorganiczna, PWN, Warszawa 1958, 692.
[27] Charakterystyka handlowego włókna światłowodowego pokrytego powłoką akrylowa: https://www.sumitomoelectric.com/cms/wp-content/uploads/ 2016/01/PureAccessA2_SMF_0112_revised_.pdf, dostęp 15 marca 2016 r.
[28] Charakterystyka włókna pomiedziowanego handlowego: http://www. ivgfiber.com/datasheet_singlemode.pdf, dostęp 15 marca 2016 r.
[29] J. Prat, P.E. Balaguer, J.M. Gene, O. Diaz, S. Figuerola, Fiber to the home technologies, Springer Science + Biznes Media, Boston 2002.
[30] IEC 60793-1-30:2010, Optical fibres. Part 1-30: Measurement methods and test procedures. Fibre proof test.
[31] Praca zbiorowa, Poradnik galwanotechnika, WNT, Warszawa 1985.

Zeszyt


PRZEMYSŁ CHEMICZNY - e-zeszyt (pdf) 2016-8 licencja: Osobista Produkt cyfrowy	55.00 zł

Prenumerata

PRZEMYSŁ CHEMICZNY - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

762.00 zł

PRZEMYSŁ CHEMICZNY - prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	1002.00 zł brutto 927.78 zł netto 74.22 zł VAT (stawka VAT 8%)

1002.00 zł

PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
PRZEMYSŁ CHEMICZNY - papierowa prenumerata roczna	960.00 zł brutto 888.89 zł netto 71.11 zł VAT (stawka VAT 8%)
PRZEMYSŁ CHEMICZNY - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

1002.00 zł

Open Access

Zeszyt

2016-8

Twój Koszyk

Zeszyt

Prenumerata

Open Access

Zeszyt

Czasopisma