Czasopismo | OCHRONA PRZED KOROZJĄ | Rocznik 2017 - zeszyt 4

Corrosion behavior of LaNi4.6Zn0.4-xSnx (x = 0÷0.4) alloys in alkaline solutions with chloride ions

10.15199/40.2017.4.3

BEATA ROŻDŻYŃSKA-KIEŁBIK

nr katalogowy: 105016
10.15199/40.2017.4.3

In the study, electrochemical corrosion of LaNi4.6Zn0.4-xSnx (x = 0÷0.4) type alloys in a strongly alkaline environment has been characterized. The influence of the presence of Cl- ions in KOH solutions on the corrosion behavior of these materials has been studied. Using the potentiokinetic method, durability of passive layers formed on LaNi4.6Zn0.4-xSnx alloys in 1M and 6M KOH solutions with chloride ions has been evaluated. All the examined LaNi4.6Zn0.4-xSnx alloys passivated efficiently in 1 M and 6 M KOH solutions. Material composition and concentration of KOH solution has significant effect on the protective properties of passive layers formed on LaNi4.6Zn0.4-xSnx type alloys. Passive layers formed on the alloys donated solely with zinc (LaNi4.6Zn0.4), in both 1 M and 6 M KOH solutions are more resistant to chloride ions with 0.3÷1.0 M concentration, whereas the addition of chloride ions to 1 M KOH solutions leads to a local degradation of the passive layer formed on the alloys with tin (LaNi4.6Zn0.2Sn0.2 and LaNi4.6Sn0.4). Keywords: LaNi4.6Zn0.4-xSnx-type alloys, polarization curves, pitting corrosion W pracy scharakteryzowano elektrochemiczną korozję stopów typu LaNi4,6Zn0,4-xSnx (x = 0÷0,4) w środowisku silnie alkalicznym. Zbadano wpływ obecności jonów Cl- w roztworach KOH na korozyjne zachowanie tych materiałów. Stosując technikę potencjokinetyczną oceniano trwałość warstw pasywnych wytworzonych na stopach LaNi4,6Zn0,4-xSnx w 1 M i 6 M roztworach KOH zawierających dodatek jonów chlorkowych. Stwierdzono, że wszystkie badane stopy LaNi4,6Zn0,4-xSnx efektywnie pasywują się w 1 M i 6 M roztworach KOH. Skład materiałów oraz stężenie roztworu KOH mają istotny wpływ na własności ochronne warstw pasywnych wytworzonych na stopach typu LaNi4,6Zn0,4-xSnx. Warstwy pasywne wytworzone na stopach modyfikowanych wyłącznie cynkiem (LaNi4,6Zn0,4) zarówno w 1 M jak i w 6 M roztworach KOH są bardziej odporne na działanie jonów chlorkowych [...]

Bibliografia

[1] Bala Henryk, Iwona Kukuła, Henryk Drulis, Alicja Hackemer. 2012. "Electrochemical hydrogenation and corrosion behaviour of LaNi5-x Bix alloys". Phys. Chem. Mech. Mater. 2 (9) : 387-392.
[2] Dymek Martyna, Beata Rozdzynska-Kielbik, Volodymyr Pavlyuk, Henryk Bala. 2015. "Electrochemical hydrogenation properties of LaNi4.6Zn0.4-xSnx alloys". J. Alloys Compd. 644 : 916-922.
[3] Rożdżyńska-Kiełbik Beata, Wacław Iwasieczko, Henryk Drulis, Volodymyr Pavlyuk, Henryk Bala. 2000. "Hydrogen equilibria characteristics of LaNi5-xZnx intermetallics". J. Alloys Compd. 298 : 237-243.
[4] Rożdżyńska-Kiełbik Beata, Przemysław Drozdek, Henryk Bala, Volodymyr Pavlyuk. 2003. "Zachowanie korozyjne stopów typu MmNi5-xZnx". Ochrona przed Korozją 11s/A : 181-186.
[5] Rożdżyńska-Kiełbik Beata, Henryk Bala, Volodymyr Pavlyuk. 2005. "Zachowanie korozyjne stopów La(Ni,Zn)5 w roztworach silnie alkalicznych". Ochrona przed Korozją 11s/A : 35-38.
[6] Rożdżyńska-Kiełbik Beata, Krystyna Giza, Volodymyr Pavlyuk. 2010. "Elektrochemiczne wodorowanie stopów MmNi5-xZnx w 6 M KOH". Ochrona przed Koroją 11 : 623-626.
[7] Szklarska-Smialowska Zuzanna. 2005. Pitting and Crevice Corrosion. Houston, TX: NACE International.
[8] Tliha M., C. Khaldi, S. Boussami, N. Fenineche, O. El-Kedim, H. Mathlouthi, J. Lamloumi. 2014. "Kinetic and thermodynamic studies of hydrogen storage alloys as negative electrode materials for Ni/MH batteries: a review". J. Solid State Electrochem. 18 : 577-593.
[9] Willems JJG. 1984. "Metal hydride electrodes stability of LaNi5-related compound". Philips J. Res. 39 : 1-93.
[10] Young K, J. Nei. 2013. "The current status of hydrogen storage alloy development for electrochemical applications". Materials 6 : 4574-4608.

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 105016 "Corrosion behavior of LaN..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2017-4 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	528.00 zł brutto 488.89 zł netto 39.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	36.00 zł brutto 29.27 zł netto 6.73 zł VAT (stawka VAT 23%)

564.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

762.00 zł

Zeszyt

2017-4

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma