Wyniki 1-2 spośród 2 dla zapytania: authorDesc:"Gaetano Palumbo"

Corrosion inhibition of carbon steel (K-55) in CO2-saturated 0.5 M KCl solution by polyacrylamide DOI:10.15199/40.2015.11.7


  Polyacrylamide (PAM) was used to investigate the inhibition efficiency on corrosion of carbon steel (K-55) in 0.5 M KCl solution with CO2 through AC impedance, polarization curves, and SEM techniques under static and hydrodynamic conditions. The electrochemical experimental results indicated that carbon steel showed active dissolution behaviour in the absence and the presence of the inhibitor PAM. However, the Nyquist diagrams showed increase in RP values in the presence of inhibitor under static and hydrodynamic conditions, thus increasing inhibition efficiency. Potentiodynamic curves suggested that the inhibitor is mixed type in nature. SEM results showed that PAM was able to influence the flow dynamic properties of solution by decreasing the friction (wall shear-stresses) between the metal surface and flowing media, thus reducing the risk of flow induced localized corrosion. Keywords: carbon steel, polyacrylamide, corrosion inhibitor, polarization Inhibitujący wpływ poli(akryloamidu) na korozję stali K55 w 0,5 M roztworze KC l nasyconym CO 2 W publikacji zawarto wyniki badań skuteczności antykorozyjnej inhibitora poliakrylamidowego (PAM) zastosowanego do hamowania procesów korozyjnych stali typu K55 w środowisku 0,5M KCl z obecnością CO2. Badania elektrochemiczne prowadzono w warunkach stacjonarnych oraz w warunkach przepływu z użyciem technik impedancyjnych i polaryzacyjnych. Obserwacje powierzchni próbki prowadzono z użyciem techniki elektronowej SEM. Wyniki badań wskazują, że stal K55 wykazała aktywność elektrochemiczną zarówno przy nieobecności jak i w obecności inhibitora PAM. Dalsze badania impedancyjne wykazały jednak, że w obecności inhibitora następuje wzrost wartości Rp badanej próbki, zarówno w warunkach stacjonarnych jak i hydrodynamicznych. To wskazuje na skuteczność hamowania korozji przez inhibitor typu PAM. Krzywe polaryzacji natomiast sugerują katodowo-anodowy charakter inhibitora. Z kolei obserwacje SEM wykazały wpływ[...]

Corrosion inhibition of K-55 carbon steel in diluted potassium chloride solution by polyacrylamide DOI:10.15199/40.2015.10.3


  The corrosion inhibition effect of the drug reducer polyacrylamide (PAM) on carbon steel (K-55) in simulated fracturing fl uid (0.3 M of KCl and 0.2 wt. % of PAM with pH 7.8) under static and hydrodynamic conditions was studied. The electrochemical experimental results indicated that the carbon steel show active dissolution behaviour in the absence and the presence of the inhibitor PAM. However, PAM acting as mixed-type inhibitor was able to promote the formation of a product layer on the metal’s surface, lowering both cathodic and anodic current density. For long exposure times, the corrosion activity of the metal increases, as result of the breakdown of the corrosion product layer and initiation of localised corrosion spots. Furthermore, it was observed that under hydrodynamic conditions PAM was not only able to promote the formation of a protective layer on the meal surface but also it was able to infl uence the fl ow dynamic properties of solution by decreasing the friction (wall shearstress) between the metal’s surface and fl owing media, thus reducing the risk of fl ow induced localized corrosion. Keywords: carbon steel, polyacrylamide, corrosion inhibitor, polarization Inhibitujący wpływ poli(akryloamidu) na korozję stali K-55 w roztworze chlorku potasu Badano inhibitujący wpływ poli(akryloamidu) (PAM), stosowanego jako dodatek redukujący lepkość, na szybkość korozji stali węglowej (K-55) w symulowanej cieczy szczelinującej (0,3 M KCl, 0,2 wt. % PAM o pH = 7,8) w warunkach statycznych i hydrodynamicznych. Wyniki badań elektrochemicznych wskazują, że stal węglowa, zarówno w obecności, jak i przy braku inhibitora PAM ulega aktywnemu rozpuszczaniu w badanym roztworze. Jednakże PAM, działając jak inhibitor typu mieszanego, promuje tworzenia się warstwy produktów korozji na powierzchni metalu, które to produkty blokując dostęp środowiska korozyjnego do powierzchni metalu, zmniejszają gęstość prądu katodowego, jak i anodowego. [...]

 Strona 1